Nitride-based heterostructure devices

ABSTRACT

A method of producing nitride based heterostructure devices by using a quaternary layer comprised of AlInGaN. The quaternary layer may be used in conjunction with a ternary layer in varying thicknesses and compositions that independently adjust polarization charges and band offsets for device structure optimization by using strain compensation profiles. The profiles can be adjusted by altering profiles of molar fractions of In and Al.

REFERENCE TO PRIOR APPLICATION

[0001] The current application claims priority to co-pending provisionalapplication serial No. 60/235,565, filed on Sep. 27, 2000.

BACKGROUND OF THE INVENTION

[0002] 1. Technical Field

[0003] The current invention relates generally to the production ofnitride based heterostructure devices. In particular, the presentinvention generally relates to nitride based heterostructures having aquaternary barrier layer that comprises AlInGaN for controlling strain,band offsets and lattice mismatches in the devices.

[0004] 2. Background Art

[0005] The large lattice mismatch between GaN, AlN and InN and thestrong piezoelectric and polarization effects in these materialssignificantly impact the electrical and optical properties of III-Nheterojunction devices. Nearly all the reported GaN-based High ElectronMobility Transistors (HEMTs) to date use strained GaN-AlGaN junctionswith alloy compositions below 35% and 15-20 nm thick barriers to avoidexceeding the critical thickness for the development of dislocationsrelieving strain. Such strain produces piezoelectric doping with about1×10¹³ cm⁻² sheet carriers. Additionally, the strain may be responsiblefor the long-term instabilities observed in some AlGaN/GaN HEMTs.

[0006] Therefore, there exists a need for a method and system ofbuilding heterojunction devices so that lattice mismatch, andconsequently strain, is controlled. As a result, the heterojunctiondevice can be designed to take advantage of piezoelectric andspontaneous polarization effects and long-term instabilities can beminimized.

SUMMARY OF THE INVENTION

[0007] The current invention provides a method and system ofindependently controlling strain and band offsets by providing nitridebased heterostructures having a quaternary layer that comprises AlInGaN(Aluminum Indium Gallium Nitride).

[0008] The current invention employs strain engineering to demonstratethe influence of piezoelectric and polarization effects in AlInGaN/GaNheterostructures having different indium content. The obtained resultsshow that the contribution to two-dimensional electron gas fromspontaneous polarization is approximately equal to the piezoelectriccharge. The piezoelectric doping not only changes the sheet electrondensity but also strongly affects the transport properties oftwo-dimensional electron gas. The obtained results show that inAlGaN/GaN heterostructures with 12% aluminum, the piezoelectric effectsincrease the sheet density-mobility product, n_(s)μ, at room temperatureby a factor of 5. Under the present invention, a low pressure MetalOrganic Chemical Vapor Deposition (MOCVD) can grow, for example,Al_(x)In_(y)Ga_(1-x-y)N—GaN heterojunctions over sapphire, 6H/4H SiC andother substrates, such as silicon or spinel.

[0009] In a first aspect of the present invention, a method of producingnitride based heterostructure devices is provided comprising the stepsof providing a substrate; and applying a quaternary layer over thesubstrate, wherein the quaternary layer comprises In.

[0010] In a second aspect of the present invention, a method ofproducing nitride based heterostructure devices is provided comprisingthe steps of: providing a substrate; applying a first layer comprisingGaN over the substrate; applying a ternary layer over the first layer,wherein the ternary layer comprises a compound selected from the groupconsisting of AlGaN and InGaN; and applying a quaternary layer over theternary layer, wherein the quaternary layer comprises AlInGaN.

[0011] In a third aspect of the present invention, a nitride basedheterostructure device is provided comprising: a substrate; a firstlayer applied over the substrate; and a quaternary layer applied overthe first layer wherein the quaternary layer comprises In.

[0012] In all these aspects, the Al and In composition might varybetween the layer thickness in order to optimize the starin distributionand the band offsets.

[0013] The exemplary aspects of the present invention are designed tosolve the problems herein described and other problems not discussed,which are discoverable by a skilled artisan.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] These and other features and advantages of this invention will bemore readily understood from the following detailed description of thevarious aspects of the invention taken in conjunction with theaccompanying drawings in which:

[0015]FIG. 1 shows the schematics of lattice mismatch and band offset inAlGaN and InGaN grown on GaN.

[0016]FIG. 2 shows on-axis X-ray of AlInGaN grown on GaN for differentIn flows (from the top to bottom) of: 0 ccm; 25 ccm; 50 ccm; 75 ccm.

[0017]FIG. 3a shows the photoluminescence of AlInGaN grown withdifferent In flows of: 1=0 ccm; 2=25 ccm; 3=50 ccm; 4=75ccm.

[0018]FIG. 3b shows the change in band-gap and lattice constant ofAlInGaN as a function of In flow.

[0019]FIG. 4a shows measured (dots and triangles) and calculated (solidline) sheet electron density in an AlInGaN/GaN heterostructure with 12%Al and different incorporations of In.

[0020]FIG. 4b shows measured (dots and triangles) and calculated (solidlines) sheet electron density in an AlInGaN—AlGaN/GaN heterostructurewith 12% Al and different incorporations of In.

[0021]FIG. 5a shows the electron Hall mobility in AlInGaN/GaNheterostructures with 12% Al and different molar fractions of Inmeasured at a temperature of 80 K.

[0022]FIG. 5b shows the calculated conduction band diagrams forAlInGaN/GaN heterostructures with 12% Al and different In content.

[0023]FIG. 5c shows the Hall mobility versus sheet density in(AlInGaN—AlGaN)/GaN at 77 K (solid dots), gated AlGaN/GaNheterostructures at 4.2 K (open circles), and AlGaN/GaN heterostructureswith different doping at 77 K (triangles).

[0024] It is noted that the drawings of the invention are not to scale.The drawings are intended to depict only typical embodiments of theinvention, and therefore should not be considered as limiting the scopeof the invention. In the drawings, like numbering represents likeelements between the drawings.

DETAILED DESCRIPTION OF THE DRAWINGS

[0025] The present invention relates to nitride based heterostructureshaving a quaternary layer that comprises AlInGaN (Aluminum IndiumGallium Nitride). The present invention can be used for a variety ofheterostructure devices, including (but not limited to) heterostructurefield effect transistors, ultraviolet and visible light emitting diodes,ultraviolet and visible photodetectors, dual infrared and ultravioletlight emitters and detectors, pyroelectric and piezoelectric devices,strain and stress sensors, and plasma wave electronics devices. It isunderstood that for the purposes of the present invention, Al meansAluminum, In means Indium, Ga means Gallium, and N means Nitrogen.

[0026] Referring now to FIG. 1, the schematics of lattice mismatch andband offset in AlGaN and InGaN grown on GaN are shown. As shown in (a),strain free growth of 50% AlGaN on GaN 10 yields a positive latticemismatch of roughly 0.003 nm. However, strain free growth of only 10%InGaN on GaN 12 is required to yield a similar negative latticemismatch. As shown in (b), the same 50% AlGaN on GaN 14 has a bandoffset of about 1.4 eV while the same 10% InGaN on GaN 16 has a bandoffset of only about 0.2 eV. Based on a linear extrapolation of latticeconstants as functions of molar fractions, it is estimated thatquaternary Al_(x)In_(y)Ga_(1-x-y)N layers with an Al/In mole fractionratio of 5 should be nearly lattice matched to GaN while the band offsetwill be about 1.2 eV.

[0027]FIG. 2 shows Secondary Ion Mass Spectroscopy (SIMS) measurementsused to determine the Al-In-Ga profiles and atomic percentages for oneembodiment of the current invention. Several series ofAl_(x)In_(y)Ga_(1-x-y)N—GaN heterojunctions were deposited withdifferent Al-precursor flows. For each series, the Ga-precursor flow waskept constant while varying the In-flow (0, 25, 50 and 75 ccm). Thethickness of the GaN and the quaternary Al_(x)In_(y)Ga_(1-x-y)N layerswere respectively kept at 100 and 200 nm. The data clearly establish theincorporation of indium fractions as large as 6% into AlInGaN quaternaryfilms. Reflection High Electron Difraction (RHEED) measurements alsoconfirmed the single crystal nature of all the Al_(x)In_(y)Ga_(1-x-y)Nquaternary layers for the growth conditions.

[0028] For all of the Al_(x)In_(y)Ga_(1-x-y)N-GaN heterojunctions,lattice mismatches and bandgaps were measured using X-ray (θ-2θ)diffraction and optical transmission versus wavelength. The bandgapvalues from transmission were in good agreement with the measured roomtemperature photoluminescence (PL) peak positions using the 4^(th)harmonic of a Q-switched Yttrium Aluminum Garnett (YAG):Nd³⁺ laserradiation (incident photon energy 4.66 eV, pulse duration 10 ns) foroptical excitation. The X-ray, SIMS and PL data were then used toestimate the alloy compositions for the quaternaryAl_(x)In_(y)Ga_(1-x-y)N layers as shown in FIGS. 3a and 3 b.

[0029]FIG. 3a shows the normalized PL intensity of the various compoundsas a function of photon energy (eV). Different In flows (0 ccm for curve1, 25 ccm for 2, 50 ccm for 3 and 75 ccm for 4) are shown. Zero In flowcorresponds to Al_(0.09)Ga_(0.91)N. The normalized peak PL intensity forthe four In flows ranges from about 3.68 eV for zero In flow 20, toabout 3.54 eV for an In flow of 75 ccm 22.

[0030]FIG. 3b shows the change in lattice constant (triangles,Angstroms) and band gap (circles, eV) as a function of In flow (ccm).Zero In flow corresponds to Al_(0.09)Ga_(0.91)N. “Zero” changecorresponds to GaN parameters.

[0031] The data clearly indicates that the addition of indium changesthe lattice constant difference (between GaN and the quaternary) about3-4 times faster than the bandgap difference. For example, comparing thedata for In flow of 75 (in arbitrary units) and the zero In flow, thelattice constant mismatch Dc varies from 0.036 Angstroms 24 to 0.005Angstroms 26, more than 7 times, whereas the energy gap discontinuityvaries only from 0.25 eV 28 to 0.12 eV 29, only a factor of 2. However,for the nearly lattice matched Al_(0.09)In_(0.02)Ga_(0.89)N—GaN junction(which corresponds to the In flow of 75), the PL measurements yieldedthe bandgap difference of only 120 meV, significantly smaller from whatwas expected using the linear interpolation of the band offsets for afixed molar fraction of aluminum.

[0032] Several Al_(x)In_(y)Ga_(1-x-y)GaN junctions with barrierthickness less than 50 run and varying alloy compositions (x from 0.1 to0.2 and y from 0.02 to 0.04) were also grown. For these heterojunctions,room temperature sheet-carrier density and mobility values ranging from1-3×10¹³ cm⁻² and 1000-1500 cm²V⁻¹sec-1 were measured. The mobilityvalues increase by about a factor of 5 upon cooling to 77 K. Thisestablishes the presence of the two-dimensional electron gas at theAl_(x)In_(y)Ga_(1-x-y)N—GaN heterojunction interface and confirms a highquality of heterointerfaces. Al_(x)In_(y)Ga_(1-x-y)N—GaN HEMTs were alsofabricated with state-of-the-art performance. The fabrication technologyfor these devices is substantially different from that for conventionalAlGaN/GaN HEMTs.

[0033] Strong piezoelectric and pyroelectric effects in AlGaN/GaNheterostructures emerged as powerful tools for the development of anovel semiconductor doping technique. In contrast to the conventionalimpurity doping, this new method does not introduce any new energylevels, carrier traps and scattering centers, which strongly affectelectrical characteristics of materials and electronic devices.

[0034] Theoretical calculations predicted the comparable contributionsof spontaneous polarization and piezoelectric effects to two-dimensionalelectron density in AlGaN/GaN heterostructures. However, so far, thereis no direct experimental evidence for these estimates. It is alsoimportant to note that the internal electric fields in pyroelectricmaterials are usually much smaller than predicted by the theory, whichdoes not account for surface and interface states. In the limiting case,when the surface state density equals or even exceeds P_(s)/q, whereP_(s) is spontaneous polarization and ‘q’ is the electron charge, thecharges trapped in surface and/or interface states can cancel the effectof spontaneous polarization, making an internal electric field vanishinside the film. This is often the case in typical ferroelectricmaterials, which makes a direct determination of the value ofspontaneous polarization and its contribution to two-dimensionalelectron gas near AlGaN/GaN heterointerface very complicated. Therefore,the direct measurements of the contribution of piezoelectric doping andelectron mobility in these AlInGaN/GaN heterostructures were focused onby measuring the properties of two-dimensional electron gas inAlInGaN/GaN heterostructures with different indium incorporation. Thisindium-controlled strain engineering allowed us to measure thepiezoelectric doping in these heterostructures.

[0035] The epilayer structures were grown by low-pressure MOCVD onconducting 6H—SiC substrates at 1000 C and 76 torr. They consisted of100 nm thick AIN buffer layer followed by approximately 0.5 mm thicksemi-insulating GaN and a nominally undoped quaternary AlInGaN barrierlayer. The different indium incorporation in the structures was achievedby keeping constant triethylgallium (TEA) and triethylaluminum (TEG)fluxes while varying the flux of trimethylindium (TMI).

[0036]FIG. 4a shows the sheet electron density (cm⁻²) as a function ofIn molar fraction for heterostructures with a barrier design consistingof a uniform AlInGaN quaternary layer. As shown in the inset, theheterostructure comprises a 6H—SiC (Silicon Carbide) substrate 32, alayer of i-GaN 34 (Gallium Nitride) and a quaternary barrier layercomprising AlInGaN 36 (Aluminum Indium Gallium Nitride). As extractedfrom Hall measurements, open circles correspond to sheet densitiesmeasured at room temperature and triangles correspond to a temperatureof 80K. Line 38 represents the expected results from calculations. Asdetermined with SEM pictures, the total thickness of the barrier variedbetween 15 and 17 nm. The aluminum molar fraction in the barrier wasdetermined from photoluminescence measurements and was approximately12%.

[0037] The lattice matching in the AlInGaN/GaN heterostructures withdifferent indium incorporation were studied by measuring the (θ-2θ)X-ray diffraction peaks arising from the (0006) AlInGaN quaternarybarriers and the underlying GaN layers. These data show the AlInGaN-GaNheterostructures to be nearly lattice matched for an estimated indium toaluminum ratio of 5, which is in good agreement with the expectationsbased upon Vegard's law. The sheet density decreases from approximately6×10¹² cm⁻² for a heterostructure with zero indium content 40 (AlGaN/GaNstructures) to a sheet density of 2-2.5×10¹² cm⁻² for the structure withclose to 2% of indium 42. Therefore, the lattice matching in AlInGaN-GaNheterostructures with 12% aluminum and 2% indium should in principlenearly eliminate the piezoelectric doping.

[0038]FIG. 4b shows the sheet electron density (cm⁻²) as a function ofIn molar fraction for heterostructures with an alternative barrierdesign consisting of a two-layer combination having a 2-3 nm AlGaN(Aluminum Gallium Nitride) ternary layer 50 followed by a 15 nm AlInGaNquaternary layer 52. As shown in the inset, the heterostructurecomprises a 6H—SiC substrate 54, a layer of i-GaN 56, a ternary layer ofAlGaN 50 and a quaternary layer comprising AlInGaN 52. As extracted fromHall measurements, open circles correspond to sheet densities measuredat room temperature and triangles correspond to a temperature of 80 K.Line 58 was calculated for an AlInGaN—AlGaN barrier with 3 nm of AlGaN,while line 60 was calculated for an AlInGaN—AlGaN barrier with 1 nm ofAlGaN. As determined with SEM pictures, the total thickness of thebarrier varied between 15 and 17 nm. The aluminum molar fraction in thebarrier was determined from photo-luminescence measurements and wasapproximately 12%.

[0039] The purpose of incorporating the thin AlGaN ternary layer 50 wasto keep the band offset at the heterointerface (barrier/GaN) constant,while controlling piezoelectric doping by incorporating indium into thetop portion of the barrier. As shown, the sheet density decreases fromapproximately 6×10¹² cm⁻² for a heterostructure with zero indium content62 (AlGaN/GaN structure) to a sheet density of 2-2.5×10¹² cm⁻² for theheterostructure with about 2% indium 64.

[0040] It should be recognized that other ternary compounds includingInGaN are suitable for use as the ternary layer. Additionally, while SiCis used as the substrate throughout the examples, it should berecognized that the current invention applies equally to the use ofother substrates including sapphire, SiC, ZnO, a spinel substrate, Si,anodized alumina, and AlN.

[0041]FIGS. 4a and 4 b show that the dependence of sheet density onindium molar fraction is nearly the same for the heterostructures withand without the 2-3 nm thick AlGaN ternary layer in the barrier region.This result points to a very small change in the conduction band offsetcaused by the incorporation of up to 2% of indium, which is in goodagreement with theoretical predictions from Vegard's law. Therefore, thedecrease in sheet density is attributed primarily to the reduction ofthe lattice mismatch and the associated strain between the AlInGaNquaternary barrier and the GaN channel layer. From the measurements ofsheet density, it is estimated that the contribution of piezoelectricdoping in the structures is approximately 4×10¹² cm².

[0042] In order to evaluate the contributions of both piezoelectric andpyroelectric (spontaneous polarization) doping, the experimental datawas compared with the calculated values of sheet density as shown byline 38 in FIG. 4a and lines 58, 60 in FIG. 4b. The calculations forAl_(0.12)In_(y)Ga_(1-0.12-y)N/GaN as shown in FIG. 4a, andAl_(0.12)In_(y)Ga_(1-0.12-y)N/ Al_(0.12)Ga N/GaN as shown in FIG. 4b,accounted for both pyroelectric and piezoelectric effects. Theparameters used in the calculations are listed in Table 1 below. TABLE 1AlInGaN/GaN parameters used in the calculations PARAMETER UNITS VALUETotal Barrier thickness (L) nm 25 (21) Thickness of AlGaN (L1) nm  5 (1)Thickness of InAlGaN (L2) nm 20 Donor concentration in cm⁻³ 10¹⁵ GaNDonor concentration cm⁻³ 3 × 10¹⁷ in AlGaN Al concentration % 12 Latticeconstant nm .3548y + .3112x + .3189(1 − x − y) Schottky barrier eV1.3x + 0.84 e₃₃ C/m² 0.97y + 1 − y − x + 1.55x e₃₁ C/m² −0.36(1 − y − x)− 0.58x − 0.57y e₃₃ GPa 200y + 389x + 267 * (1 − x − y) e₁₃ GPa 94y +99x + 158(1 − x − y) In_(y)Al_(x)Ga_(1−y−x)N/GaN eV 0.75 ΔEg Conductionband discontinuity In_(y)Al_(x)Ga_(1−y−x)N band eV 1.9y + 3.4 * (1 − y −x) + 6.2x gap In_(y)Al_(x)Ga_(1−y−x)N C/m² −0.052 * x − 0.029spontaneous polarization at zero strain Dielectric constant of AlN  8.5

[0043] The calculated values of sheet density, including only thepiezoelectric effects and the spontaneous polarization, are close to themeasured values. This indicates that the piezoelectric and pyroelectriceffects are the only major contributors to two-dimensional electron-gas.This is expected since the background sheet carrier density due tounintentional doping of the quaternary barrier (AlInGaN) and the channelsemi-insulating GaN layer was measured to be not more than 1×10¹² cm⁻².These measurements were made on thick individual layers. Also, thecalculated sheet electron density falls from approximately 5×10¹² cm⁻²for AlGaN/GaN heterostructures (0% In) to 2.7×10¹² cm⁻² for(AlInGaN—AlGaN)/GaN and 2.4×10¹² cm⁻² for AlInGaN/GaN heterostructureswith up to 2% of indium. Thus, the calculated contribution of thepiezoelectric effects (piezoelectric doping) is approximately 2.5×10¹²cm⁻², which is about 30% less than measured experimentally. As can beseen from FIGS. 4a and 4 b, the data confirms a considerablecontribution from the spontaneous polarization.

[0044] The reduction of strain in AlInGaN/GaN heterostructures with theincorporation of indium not only decreases piezoelectric doping, butalso strongly reduces two-dimensional electron mobility. The measuredelectron Hall mobility, μ_(H), in (AlInGaN—AlGaN)/GaN heterostructuresat 80 K is shown in FIG. 5a. The incorporation of 2% indium reduces themobility by more than three times from 7,300 cm²/Vs for zero In content70 to approximately 2,000 cm²/Vs for 2% In 72. Nearly the same reductionin 80 K Hall mobility was also measured for AlInGaN/GaNheterostructures. At 300 K, the mobility in (AlInGaN—AlGaN)/GaNheterostructures decreased by half from 1,200 cm² Ns for 0% indium to600 cm²/Vs for 2% indium. This reduction of Hall mobility in AlInGaN/GaNheterostructures is attributed to the suppression of piezoelectriceffects and the associated piezoelectric doping.

[0045]FIG. 5b shows the calculated band diagrams of AlInGaN/GaNheterostructures with different Indium content. The energy (eV) for eachband is shown as a function of distance (nm). Curve 80 corresponds to 0%In incorporation, curve 82 corresponds to 1% In, and curve 84corresponds to 2% In. Dotted line 86, dotted-dashed line 88 and dashedline 90 mark the Fermi level positions for curves 80, 82 and 84,respectively. Thick solid lines show ground energy levels inside thetriangle quantum wells. As seen, the ground state energy and Fermi levelin the triangular quantum wells near AlInGaN/GaN heterointerface havehigher indium content in the regions of lower electric field(proportional to the band bending) and, thus, have lower quantization.As a result, electrons are becoming less two-dimensional and morebulk-like with lower mobility. Note that the measured decrease in Hallmobility with decease in sheet electron density from the loss ofpiezoelectric doping in the nearly lattice matched AlInGaN/GaNheterostructures is in good agreement with μ_(H) (sheet density) dataobtained in AlGaN/GaN heterostructures.

[0046]FIG. 5c shows two-dimensional Hall mobility (at 80 K) as afunction of sheet electron density in the (AlInGaN—AlGaN)/GaNheterostructures with that for AlGaN/GaN heterostructures. The resultsclearly show the important role of the piezoelectric effects in bothdoping and the transport properties of two-dimensional electron gas inAlInGaN-GaN heterojunctions.

[0047] The foregoing description of the preferred embodiments of thisinvention has been presented for purposes of illustration anddescription. It is not intended to be exhaustive or to limit theinvention to the precise form disclosed, and obviously, manymodifications and variations are possible. Such modifications andvariations that may be apparent to a person skilled in the art areintended to be included within the scope of this invention as defined bythe accompanying claims.

What is claimed is:
 1. A method of producing nitride basedheterostructure devices comprising the steps of: providing a substrate;and applying a quaternary layer over the substrate wherein thequaternary layer includes In.
 2. The method of claim 1, wherein thesubstrate comprises one of the group comprising sapphire, SiC, ZnO, aspinel substrate, Si, anodized alumina, and AlN.
 3. The method of claim1, wherein the quaternary layer further includes Al, Ga andN.
 4. Themethod of claim 1, further comprising applying a second layer positionedbetween the substrate and the quaternary layer.
 5. The method of claim4, wherein the second layer includes GaN.
 6. The method of claim 1,wherein the quaternary layer includes the compound AlInGaN.
 7. Themethod of claim 6, wherein the quaternary layer includes about a 20% to30% molar fraction of Al.
 8. The method of claim 7, wherein thequaternary layer further includes about a 2% to 5% molar fraction of In.9. A method of producing nitride based heterostructure devicescomprising the steps of: providing a substrate; applying a first layerincluding GaN over the substrate; applying a ternary layer over thefirst layer, wherein the ternary layer includes a compound selected fromthe group comprising AlGaN and InGaN; and applying a quaternary layerover the ternary layer, wherein the quaternary layer includes AlInGaN.10. The method of claim 9, wherein the substrate includes one of thegroup comprising sapphire, SiC, ZnO, a spinel substrate, Si, anodizedalumina, and AlN.
 11. The method of claim 9, wherein the quaternarylayer includes about a 20% to about 30% molar fraction of Al.
 12. Themethod of claim 11, wherein the quaternary layer further includes abouta 2% to about 5% molar fraction of In.
 13. A nitride basedheterostructure device comprising: a substrate; a first layer appliedover the substrate; and a quaternary layer applied over the first layerwherein the quaternary layer includes In.
 14. The device of claim 13,wherein the substrate includes one of the group comprising sapphire,SiC, ZnO, a spinel substrate, Si, anodized alumina, and AlN.
 15. Thedevice of claim 13, wherein the first layer includes GaN.
 16. The deviceof claim 13, wherein the quaternary layer includes AlInGaN.
 17. Thedevice of claim 13, wherein the device is used as one of the groupcomprising of a field effect transistor, an ultraviolet light emittingdiode, a visible light emitting diode, an ultraviolet lightphotodetector, a visible light photodetector, a dual infrared lightemitter and detector, a dual ultraviolet light emitter and detector, apyroelectric device, a piezoelectric device, a strain sensor, a stresssensor, and a plasma wave electronics device.
 18. The device of claim 13further comprising a ternary layer applied between the first layer andthe quaternary layer.
 19. The device of claim 18, wherein the ternarylayer includes a compound selected from the group comprising AlGaN andInGaN.